MCH21
Ceramic capacitors
Multi-layer ceramic chip capacitors
MCH21
(2012 (0805) size, chip capacitor)
Features
1) Miniature, high capacitance
2) Achieved high capacitance by thin and multi layer technology
3) Lead-free plating terminal
4) No polarity
Quick Reference
The design and specifications are subject to change without prior notice. Please check the most recent technical
specifications prior to placing orders or using the product. For more detail information regarding packaging style code,
please check product designation.
Thermal compensation
Part No.
MCH21
Size code
2012
(0805)
Temperature characteristics
code (ppm/°C)
A(AN)
0
±
30
(CG)(C0G)
Operating temp. range
(°C)
−55
to
+125
Rated voltage
(V)
50
Capacitance(pF)
2,200 to 3,300 (E12 Series)
3,900 to 5,600 (E12 Series)
6,800 to 10,000 (E12 Series)
Capacitance
tolerance
J(
±
5%)
Thickness
(mm)
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
∗
: 0.5pF/0.75pF/2pF/3pF/4pF/5pF/6pF/7pF/8pF/9pF available
High dielectric constant
Part No.
Size code
Temperature characteristics
code
Operating temp. range
(
°C)
−25
to
+85
Rated voltage
(V)
50
25
CN
Capacitance(pF)
220 to 47,000(E6 Series)
68,000(E6 Series)
100,000(E6 Series)
150,000 to 220,000(E6 Series)
220 to 47,000(E6 Series)
68,000(E6 Series)
100,000(E6 Series)
150,000 to 220,000(E6 Series)
330,000 to 1,000,000(E6 Series)
1,500,000 to 2,200,000(E6 Series)
3,300,000 to 4,700,000(E6 Series)
10,000,000(E3 Series)
1,000 to 220,000(E3 Series)
470,000(E3 Series)
1,000,000(E3 Series)
2,200,000 to 4,700,000(E3 Series)
10,000,000(E3 Series)
22,000,000(E3 Series)
1,000 to220,000(E3 Series)
470,000(E3 Series)
1,000,000(E3 Series)
2,200,000 to 4,700,000(E3 Series)
10,000,000(E3 Series)
22,000,000(E3 Series)
Capacitance
tolerance
Thickness
(mm)
±
10%
(B)
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
K (
±
10%)
±
15%
(R) (X7R)
−55
to
+125
50
25
16
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
0.85
±
0.15
1.25
±
0.2
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
±
15%
(X5R)
MCH21
2012
−55
to
+85
10
06.3
50
25
+30%, −80%
(F)
FN
+22%, −82%
(Y5V)
−25
to
+85
16
10
06.3
50
25
Z (+80%,
−20%)
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
−30
to
+85
16
10
06.3
1/11
MCH21
Ceramic capacitors
External dimensions
(Unit : mm)
0.2Min.
0.6Min.
T
T
2.0
±
0.1
∗1
CN charac.
CN charac.
FN charac.
∗2
CN charac.
CN charac.
FN charac.
∗1
Product thickness(mm)
0.6
±
0.1
0.85
±
0.15
1.25
±
0.2
1.25
±
0.1
∗2
:
:
:
:
:
:
2.0
±
0.2(mm)
2.0
±
0.2(mm)
2.0
±
0.2(mm)
1.25
±
0.2(mm)
1.25
±
0.2(mm)
1.25
±
0.2(mm)
330,000 to 1,000,000pF
3,300,000 to 10,000,000pF
2,200,000 to 10,000,000pF
330,000 to 1,000,000pF
3,300,000 to 10,000,000pF
2,200,000 to 10,000,000pF
Product designation
Code Prduct thickness
K
P
1.25mm
Packing specification
Pulastic tape(width 8mm, pitch 4mm)
Reel
φ180mm
(7in.)
φ180mm
(7in.)
Basic ordering unit(pcs.)
4,000
2,000
0.6,0.85mm
Paper tape(width 8mm, pitch 4mm)
Reel(φ180mm):compatible with EIAJ ET-7200A
Part No.
Packaging Style
M C H
Rated voltage
Code Voltage
8
4
3
2
5
6.3V
10V
16V
25V
50V
2 1
2
F
N
1 0 5
Z
Nominal
capacitance
3-digit
designation
accordijg
to IEC
K
Capacitance tolerance
Tolerance
Code
J
K
Z
Temperature characteristic code
:Refer to quick reference table.
±
5%(11pF or more)
±
10%
+80%, −20%
Product No.list
•Thermal
compensation capacitors
Capacitance
(pF)
2,200
2,700
3,300
3,900
4,700
5,600
6,800
8,200
10,000
Temperature
Rated voltage(V)
Tolerance Product thickness(mm)
0.6
±
0.15
J (
±
5%)
0.85
±
0.15
1.25
±
0.15
A AN(CG) (COG) (CH)Characteristic
25V
Product No.
MCH215A (AN) 222Jk
MCH215A (AN) 272Jk
MCH215A (AN) 332Jk
MCH215A (AN) 392Jk
MCH215A (AN) 472Jk
MCH215A (AN) 562Jk
MCH215A (AN) 682Jk
MCH215A (AN) 822Jk
MCH215A (AN) 103Jk
2/11
MCH21
Ceramic capacitors
•High
dielectric constant capacitors
Capacitance
(pF)
Temperature
Rated voltage(V)
Tolerance Product thickness(mm)
220
330
470
680
1,000
1,500
2,200
3,300
4,700
6,800
10,000
15,000
22,000
33,000
K (
±
10%)
47,000
68,000
100,000
150,000
220,000
330,000
470,000
680,000
1,000,000
1,500,000
2,200,000
3,300,000
4,700,000
10,000,000
0.6
±
0.1
0.85
±
0.15
CN (R) (B) (X7R)Characteristic
50V
25V
Product No.
Product No.
MCH215CN221KK
MCH215CN331KK
MCH215CN471KK
MCH215CN681KK
MCH215CN102KK
MCH215CN152KK
MCH215CN222KK
MCH215CN332KK
MCH215CN472KK
MCH215CN682KK
MCH215CN103KK
MCH215CN153KK
MCH215CN223KK
MCH215CN333KK
MCH215CN473KK
MCH215CN683KK
MCH215CN104KP
MCH212CN154KP
MCH212CN224KP
16V
Product No.
CN (X5R)Characteristic
10V
Product No.
6.3V
Product No.
1.25
±
0.2
MCH213CN334KP
MCH213CN474KP
MCH213CN684KP
MCH213CN105KP
MCH214CN155KK
MCH214CN225KK
MCH214CN335KP
MCH214CN475KP
MCH218CN106KP
0.85
±
0.15
1.25
±
0.2
Capacitance
(pF)
Temperature
Rated voltage(V)
Tolerance Product thickness(mm)
1,000
2,200
4,700
10,000
22,000
47,000
Z (
+
80%,
100,000
−20%)
220,000
470,000
1,000,000
2,200,000
4,700,000
10,000,000
22,000,000
0.6
±
0.15
50V
Product No.
MCH215FN102ZK
MCH215FN222ZK
MCH215FN472ZK
MCH215FN103ZK
MCH215FN223ZK
MCH215FN473ZK
MCH215FN104ZK
MCH215FN224ZK
25V
Product No.
FN (F) (Y5V)Characteristic
16V
Product No.
10V
Product No.
6.3V
Product No.
MCH212FN474ZK
0.85
±
0.15
0.6
±
0.15
0.85
±
0.15
1.25
±
0.2
MCH213FN105ZK
MCH213FN225ZK
MCH213FN475ZK
MCH214FN106ZP
MCH218FN226P
3/11
MCH21
Ceramic capacitors
•Performance
and test method
No.
1
Items
Appearance and
dimensions
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
No marked defects shall be allowed As per 4.4 of JIS C 5101-1.
As per 4.5 of JIS C 5101-10
for appearance.
Dimensions shall be as specified the Using a Magnifier.
clause 4.
No dielectrical breakdown or other
damage shall be allowed.
2
Withstanding voltage
As per 4.6 of JIS C 5101-1.
As per 4.6.4 of JIS C 5101-10
Voltage shall be applied as per Table1.
Table 1
Charac-
Voltage
teristic
A, AN
300% Rated voltage
CN
250% Rated voltage
FN
Voltage shall be applied for 1 to 5s with
50mA charging and discharging curent.
3
Insulation resistance
Not less than 10000MΩ or
500MΩ
µF,
whichever is less.
(For products with rated voltage less
than 16V, it is not less than 10000MΩ
or 100MΩ
µF,
whichever is less.)
As per 4.5 of JIS C 5101-1.
As per 4.6.3 of JIS C 5101-10
Measurements shall be made after
60+/−5s period of the rated voltage
applied.
As per 4.7 of JIS C 5101-1.
As per 4.6.1 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
Table 2
Charac-
Frequency Voltage
teristic
< 1000 pF
> 1000 pF
−
1+/−0.1MHz
1+/−0.1kHz
A, AN
1+/−0.1Vrms. 1+/−0.1Vrms.
CN
1+/−0.1kHz
1+/−0.1Vrms.
FN
4
Capacitance
Capacitance shall be
within specified tolerance range.
5 Dielectric loss tangent
A, AN
CN
tan
δ
< 0.1%
−
Rated voltage=50,25V
tan
δ
< 3.0%
−
Rated voltage=16,10V
tan
δ
< 5.0%
−
Rated voltage=6.3V
tan
δ
< 10.0%
−
Rated voltage=50V
tan
δ
< 5.0%
−
Rated voltage=25V
tan
δ
< 7.5%
−
Rated voltage=16V
tan
δ
< 10.0%
−
Rated voltage=10V, 6.3V
tan
δ
< 12.5%
−
As per 4.8 of
JIS C 5101-1.
As per 4.6.2 of
JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
FN
4/11
MCH21
Ceramic capacitors
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
Temperature coefficient shall be calculated
at 20°C and 85°C.
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
If required, measurements shall be made
at a given temperature.
Temperature coefficient shall be calculated
at 20°C.
6 Temperature
characteristic
A, AN
0+/−30ppm /
°C
(−55°C to
+125°C)
X7R
R
B
X5R
+/−15%
(−55°C to
+125°C)
+/−10%
(−25°C to
+85°C)
+/−15%
(−55°C to
+85°C)
CN
FN
+30%, −80%
(−25°C to
+85°C)
+22%, −82%
(−30°C to
+85°C)
7 Solderability
More than 3/4 of each end
termination shall be covered with
new solder.
As per 4.15.2 of JIS C 5101-1.
As per 4.11 of JIS C 5101-10
The solder specified in JIS Z 3282 H63A
shall be used. Ans the flux containing 25%
rosin and ethanol solution shall be used.
The specimens shall be immersed into the
solder at 235+/−5°C
for 2+/−0.5s
So that both end terminations are
completely under solder.
8
Resistance
to solderin
heat
Appearance Without mechanical damage.
Change
rate from
initial value
A, AN
Within
+/−2.5%
Within
+/−7.5%
Within
+/−20%
CN
FN
Dielectric
loss
tangent
Insulation
resistance
Within specified initial value.
As per 4.14 of
JIS C 5101-1.
As per 4.10 of
JIS C 5101-10
The solder specified in JIS Z 3282. H63A
shall be used.
The specimens shall be immersed into the
solder at 260+/−5
°C
for
5+/−0.5s so that
both end terminations are completely
under the solder.
Pre-heating at 150+/−10
°C
for 1 to 2min
Initial measurements prior to test shall be
performed after the thermal
Pre-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Table3
Charac-
teristic
A, AN
CN, FN
Time
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
9 End termination
adherence
24+/−2 h
48+/−4 h
Without peeling or sign of
peeling shall be allowed
on the end terminations.
As per 4.13 of JIS C 5101-1.
As per 4.8 ofJIS C 5101-10
A 5N weight for
10+/−1s shall be applied
to the soldered specimens as shown by the
arrow mark in the below sketch.
Applied pressure
Substrate
Capacitor
5/11
京公网安备 11010802033920号
EEWORLD