Disc Ceramic Capacitors
Professional Ceramic Capacitors - Class I, II and III
MIL-STD-202F
The professional ceramic disc capacitors were specially
developed for applications in severe environmental condi-
tions, high humidity, temperature, gas, vapor and solvents.
The capacitors are flame retardant epoxy coated, meeting
UL 94-V0 flammability specifications. The capacitors are
100% screened on following electrical parameters:
Capacitance, loss factor, test voltage. After the 100% test,
the capacitors are audited on its electrical and mechanical
parameters with following AQL:
Electrical parameters: 0.065% level II
Mechanical parameters: 0.65% level II
The capacitors withstand the following reliability essays:
Terminal strength: method 211 – condition A
Resistance to solvents: method 215
Resistance to soldering heat: method 210 – condition B
Solderability: method 208
Thermal shock: method 107 – condition A
Humidity (steady state): method 103 – condition D
Life (at elevated ambient temperature): method 108 –
condition D
Operating temperature and storage: -55... +125º C
0.6 ± 0.1
(0.024) (0.004)
Ø mm =
0.8 ± 0.1
(0.031) (0.004)
Ø mm =
Preferred lead spacing F = 5 (0.197)
millimeters (inches)
Lead Spacing
F
2.5 (0.100)
5 (0.200)
6 (0.250)
7.5 (0.300)
10 (0.400)
D
A
E
B
C
—
O
X
R
W
Digit 8
DIMENSIONS
Digit 9
(ø)
A
NP0
1pF... 2.7 pF
millimeters (inches)
T max.
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.5 (0.138)
3.5 (0.138)
4.0 (0.157)
D±2
(0.079)
4.0 (0.157)
4.0 (0.157)
4.0 (0.157)
5.0 (0.197)
6.0 (0.236)
7.0 (0.276)
8.0 (0.315)
9.0 (0.354)
10.0 (0.394)
11.0 (0.433)
13.0 (0.512)
15.0 (0.591)
19.0 (0.748)
Available
Lead Spacing
A,B,D,E,O,R
A,B,D,E,O,R
A,B,D,E,O,R
A,B,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,E,O,R,X
A,B,C,E,O,R,X
A,B,C,E,O,R,W
B,C,R,W
B,C,R,W
B,C
A
5.6pF... N1500
8.2 pF
A
Others
B
C
D
E
F
G
H
J
K
M
(E), (X), (W): upon request
23
Disc Ceramic Capacitors
General Specifications - Class III Professional
DIELECTRIC - CLASS III
A thin dielectric layer is grown on a disc of conductive
ceramic. Very large capacitances can be obtained due to
reduced thickness of this barrier layer and its inherently
high dielectric constant. Due its small dimensions, they are a
less expensive replacement of multilayer ceramic or poly-
ester capacitors.
Ø = 0.6 ± 0.1
(0.024) (0.004)
DIMENSIONS
Digit 9
of P.N.
(ø)
A
B
C
D
E
F
G
H
J
K
millimeters (inches)
T max.
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.0 (0.118)
3.5 (0.138)
4.0 (0.157)
D±2
(0.079)
4.0 (0.157)
5.0 (0.197)
6.0 (0.236)
7.0 (0.276)
8.0 (0.315)
9.0 (0.354)
10.0 (0.394)
11.0 (0.433)
13.0 (0.512)
15.0 (0.591)
Available
Lead Spacing
A,B,D,E,O,R
A,B,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,D,E,O,R,X
A,B,C,E,O,R,X
A,B,C,E,O,R,X
A,B,C,E,O,R,W
B,C,R,W
B,C,R,W
2.5 (0.100)
5 (0.200)
6 (0.250)
7.5 (0.300)
10 (0.400)
Preferred lead spacing
F = 5 (0.197)
millimeters (inches)
Lead Spacing
F
D
A
E
B
C
—
O
X
R
W
Digit 8 of P.N.
(E), (X), (W): upon request
PERFORMANCE CHARACTERISTICS CLASS III
Measured at
Dissipation
Factor
Capacitance
Tolerance
Climatic
Category
Insulation
Resistance
@ V
R
Dielectric Strength
NOTE: Charging
current limited
to 50 mA
Operating
Temperature
Range (ºC)
Y5P
Y5U
Y5V
Between
leads
Body
insulation
1.0 kHz / 0.1 Vrms / 25ºC
C
R
≤
22 nF
→
Y5V, Y5U
≤
7.5%
C
R
> 22 nF
→
Y5V, Y5P
≤
5.0%
Y5P
→
±20% / -20 +50%
Y5U
→
±20% / -20 +80%
Y5V
→
±20% / -20 +80%
55 / 085 / 56
≥12
M
Ω
4.7 nF...100 nF
→ ≥
10 M
Ω
200 nF
→ ≥
1 M
Ω
≥
100 M
Ω
Vt = 1.25 V
R
V
R
= 25V Vt = 100V (DC)
V
R
= 50V Vt = 150V (DC)
-55... +125 Epoxy Coated
Note: Damp Heat Steady State: 90... 95% R.H. 40ºC / 21 days. No voltage to be applied.
26
Disc Ceramic Capacitors
Ordering Code
M
A
E
A
A
Tolerance
C = ±0.25 pF
D = ±0.50 pF
J = ±5%
K = ±10%
M = ±20%
S = -20+50%
Z = -20+80%
P = 0+100%
Capacitor Diameter
± 2 (0.079)
A = 4 (0.157)
B = 5 (0.197)
C = 6 (0.236)
D = 7 (0.276)
E = 8 (0.315)
F = 9 (0.354)
G = 10 (0.394)
H = 11 (0.433)
J = 13 (0.512)
K = 15 (0.591)
M* = 19 (0.748)
*Wire 0.8 (0.031) recommended
Packaging
Cardboard Strips
A
=
Bulk
E
= 5 (0.197) ± 1 (0.039) free wire length
C
= 10 (0.394) ± 1 (0.039) free wire length
D
= 25 (0.984) ± 1 (0.039) free wire length
Taping
Reel
Avisert
Panasert
Lead Forming
mm
2.5 ±0.5
+0.6
5 -0.2
+0.6
6 -0.2
+1
7.5 -0.5
+0.5
10 -1.0
+1
12.5 -0.5
inches
.1 ± .025
.2 ± .025
.25 ± .025
.3 ± .05
.4 ± .05
.5 ± .05
D
A
E
B
C
P
–
O
X
R
W
–
–
N
–
Q
–
–
Finishing
Diam
≤9
(0.354) and
F = 5.00 (0.197)
For every other:
H
Ammo
Pack
L
L
J
L
L
Avisert
Panasert
I
M M
K M M
Coating does not
surpass the bend
Low Voltage
A = Phenolic
General
(
Purpose
)
Q = Waxed phenolic
S = Epoxy (Professional) cap. diameter
≤
8 (0.315)
D = Epoxy (Professional) cap. diameter
> 8 (0.315)
High Voltage
F = Measured
from the
center of
leads
C = Epoxy wire diameter
I = Epoxy wire diameter
Please note that not all code combinations
are either possible or available.
L = Phenolic wire diameter
0.6 ± 0.1
(0.024) (0.004)
0.8
0.1
±
(0.031) (0.004)
0.6 ± 0.1
(0.024) (0.004)
5