NICKEL CADMIUM BATTERIES: INDIVIDUAL DATA SHEET
P-120SCJS
4/5SC size (KR23/34) Type: R
Dimensions (with tube)
(mm)
Typical Charge Characteristics
2.0
1.8
Charge: 1200mA(1It)x 1.5hrs.
Voltage (V)
1.6
1.4
1.2
1.0
10˚C
20˚C
40˚C
23.0
+ 0
-
1.0
(
+
)
0.8
0
10
20
30
40
50
60
70
80
90
100
Charge Time (minutes)
34.0
+ 0
-
1.5
Typical Discharge Characteristics
1.8
1.6
Charge: 1200mA(1It)x 1.5hrs., 20˚C
Discharge Temp.: 20˚
Voltage (V)
( )
1.4
1.2
1.0
0.8
20A
10A
Specifications
Diameter
Height
Approximate
Weight
Nominal Voltage
Rated (Min.)
Approx. Internal impedance at
1000Hz at charged state
Standard
Charge
Rapid***
Charge
Standard
Discharge
Capacity*
Average**
mm
23.0 +0/-1.0
34.0 +0/-1.5
Grams
37g
inch
0.89 +0/-0.02
1.34 +0/-0.06
Ounces
1.31
1.2V
1300mAh
1200mAh
6mΩ
0
1
2
3
4
5
6
7
8
9
10
Discharge Time (minutes)
Voltage (V)
Ambient
Temperature
Rapid
Discharge
< 2 years
< 6 months
Storage
< 1 month
< 1 week
120mA (0.1It) x 16 hrs.
1200mA (1It) x 1.5 hrs.
˚C
˚F
0˚C to 45˚C 32˚F to 113˚F
10˚C to 40˚C 50˚F to 104˚F
-20˚C to 65˚C
-20˚C to 35˚C
-20˚C to 45˚C
-20˚C to 55˚C
-20˚C to 65˚C
-4˚F to 149˚F
-4˚F to 95˚F
-4˚F to 113˚F
-4˚F to 131˚F
-4˚F to 149˚F
1.8
1.6
1.4
1.2
1.0
0.8
Charge: 1200mA(1It)x 1.5hrs., 20˚C
Discharge: 1200mA(1It)
20˚C
0˚C
45˚C
0
10
20
30
40
50
60
70
80
Discharge Time (minutes)
* 0.2It discharge capacity after charging at 0.1It for 16 hours.
** For reference only.
*** Refer to “Charge Methods for Ni-Cd Batteries”
Battery performance and cycle life are strongly affected by how they
are used. In order to maximize battery safety, please consult Panasonic
when determining charge / discharge specs, warning label contents and
unit design.
Note:
[It] was previously expressed as [C]. [It] is an IEC standard expression
for the amount of charge or discharge current and is expressed as:
It(A) = Cn (Ah)/1h.
• [It] is the reference test current in ampres
• [Cn] is the rated capacity of the cell or battery in Ampere-hours.
n = the time base [hours] for which the rated capacity is declared
NICKEL CADMIUM HANDBOOK, PAGE 51
AUGUST 2003