GRM1555C1H1R5BA01-01A
■
Specifications and Test Methods
Item
No.
1 Rated Voltage
Specification
Shown in Rated value.
Test Method (Ref. Standard:JIS C 5101, IEC60384)
The rated voltage is defined as the maximum voltage which may be applied continuously to the capacitor.
When AC voltage is superimposed on DC voltage, V
P-P
or V
O-P
, whichever is larger, should be maintained
within the rated voltage range.
Visual inspection.
Using Measuring instrument of dimension.
Measurement Point :
Between the terminations
Test Voltage :
300% of the rated voltage
Applied Time :
1s to 5s
Charge/Discharge Current : 50mA max.
Measurement Temperature: Room Temperature
Measurement Point :
Between the terminations
Measurement Voltage :
Rated Voltage
Charging Time :
2min
Charge/Discharge Current : 50mA max.
Measurement Temperature: Room Temperature
Measurement Frequency : 1.0+/-0.1MHz
Measurement Voltage :
0.5 to 5.0Vrms
2 Appearance
3 Dimension
4 Voltage Proof
No defects or abnormalities.
Shown in Rated value.
No defects or abnormalities.
5 Insulation Resistance(I.R.)
More than 10000MΩ
6 Capacitance
Shown in Rated value.
7 Q or Dissipation Factor (D.F.)
Q≧400+20C C:Nominal Capacitance(pF)
Measurement Temperature : Room Temperature
Measurement Frequency : 1.0+/-0.1MHz
Measurement Voltage :
0.5 to 5.0Vrms
The capacitance change should be measured after 5 minutes at each specified temperature stage.
Capacitance value as a reference is the value in "*" marked step.
The capacitance drift is calculated by dividing the differences between the maximum and minimum measured values in the step 1,3 and 5 by the capacitance
value in step 3.
8 Capacitance
Temperature
Characteristics
No bias
Nominal value of the temperature coefficient is shown in Rated value.
But, the Capacitance Change under Reference Temperature is shown in
Table A.
Capacitance Drift:Within +/-0.2% or +/-0.05pF (Whichever is larger)
Measurement Voltage :
Less than 1.0Vrms (Refer to the individual data sheet)
Step
1
2
3
*
4
5
Temperature(°C)
Reference Temp. +/-2
Min. Operating Temp. +/-3
Reference Temp. +/-2
Max. Operating Temp. ±3
Reference Temp. +/-2
Applying Voltage
No bias
GRM1555C1H1R5BA01-01A
Item
No.
9 Adhesive Strength of
Termination
Specification
No removal of the terminations or other defect should occur.
Test Method (Ref. Standard:JIS C 5101, IEC60384)
Solder the capacitor on the test substrate shown in Fig.3.
Applied Force :
5N
Holding Time :
10+/-1½
Applied Direction :
In parallel with the test substrate and vertical with the capacitor side
Solder the capacitor on the test substrate shown in Fig.3.
Kind of Vibration :
A simple harmonic motion 10Hz to 55Hz to 10Hz
Vibration Time :
1min
Total Amplitude :
1.5mm
This motion should be applied for a period of 2hours in each 3 mutually perpendicular directions(total of 6hours).
10 Vibration
Appearance
No defects or abnormalities.
Capacitance Within the specified initial value.
Q or D.F.
Within the specified initial value.
11 Substrate
Bending Test
Appearance
No defects or abnormalities.
Capacitance Within +/-5% or +/-0.5pF (Whichever is larger)
Change
Solder the capacitor on the test substrate shown in Fig.1.
Pressurization Method :
Shown in Fig.2.
Flexure :
1mm
Holding Time :
5+/-1s
Soldering Method :
Reflow soldering
Test Method :
Flux :
Preheat :
Solder :
Test Temp. :
Test Time :
Test Method :
Solder :
Solder Temp. :
Test Time :
Preheat Temp. :
Preheat Time :
Solder bath method
Solution of rosin ethanol 25(mass)%
80℃ to 120℃、10s to 30s
Sn-3.0Ag-0.5Cu(Lead Free Solder)
245+/-5℃
2+/-0.5s
Solder bath method
Sn-3.0Ag-0.5Cu(Lead Free Solder)
270+/-5℃
10+/-0.5s
120℃ to 150℃
1min
12 Solderability
95% of the terminations is to be soldered evenly and continuously.
13 Resistance
to Soldering
Heat
Appearance
No defects or abnormalities.
Capacitance Within +/-2.5% or +/-0.25pF (Whichever is larger)
Change
Q or D.F.
Within the specified initial value.
I.R.
Voltage
Proof
Within the specified initial value.
No defects.
Post-treatment :
Let sit for 24+/-2hours at room temperature, then measure.
14 Temperature
Sudden
Change
Appearance
No defects or abnormalities.
Solder the capacitor on the test substrate shown in Fig.3.
5 cycles
Cycles :
Step
1
2
3
4
Temperature(℃)
Min.Operating Temp. +0/-3
Reference Temp.
Max.Operating Temp. +3/-0
Reference Temp.
Time (min)
30+/-3
2 to 3
30+/-3
2 to 3
Capacitance Within +/-2.5% or +/-0.25pF (Whichever is larger)
Change
Q or D.F.
Within the specified initial value.
I.R.
Voltage
Proof
Within the specified initial value.
No defects.
Post-treatment :
Let sit for 24+/-2hours at room temperature, then measure.
GRM1555C1H1R5BA01-01A
Item
Specification
No.
15 High
Appearance No defects or abnormalities.
Temperature
High Humidity
Capacitance Within +/-7.5% or +/-0.75pF (Whichever is larger)
(Steady)
Change
Q or D.F.
Q≧100+10C/3 C:Nominal Capacitance(pF)
I.R.
More than 500MΩ or 25Ω½F (Whichever is smaller)
Test Method (Ref. Standard:JIS C 5101, IEC60384)
Solder the capacitor on the test substrate shown in Fig.3.
40+/-2℃
Test Temperature :
Test Humidity :
90%RH to 95%RH
Test Time :
500+/-12h
Test Voltage :
Rated Voltage
Charge/Discharge Current : 50mA max.
Post-treatment :
Let sit for 24+/-2hours at room temperature, then measure.
16 Durability
Appearance
No defects or abnormalities.
Capacitance Within +/-3% or +/-0.3pF (Whichever is larger)
Change
Q or D.F.
Q≧200+10C C:Nominal Capacitance(pF)
I.R.
More than 1000MΩ or 50Ω½F (Whichever is smaller)
Solder the capacitor on the test substrate shown in Fig.3.
Test Temperature :
Maximum Operating Temperature+/-3℃
Test Time :
1000+/-12h
Test Voltage :
200% of the rated voltage
Charge/Discharge Current : 50mA max.
Post-treatment :
Let sit for 24+/-2hours at room temperature, then measure.
Table A Capacitance Change between at Reference Temp. and at each Temp. (%)
-55℃
-30℃
-10℃
Char.
Max.
Max.
Min.
Min.
Max.
Min.
5C
0.58
-0.24
0.4
-0.17
0.25
-0.11
GRM1555C1H1R5BA01-01A
Substrate Bending Test
・Test
Substrate
Material : JIS C 6484 Copper-clad laminated sheets for PCBs (Glass fabric base, epoxy resin)
Thickness :
0.8mm
Copper Foil Thickness: 0.035mm
Kind of Solder : Sn-3.0Ag-0.5Cu
Land
b
4.5
40
c
c
Series
GRM15
Dimension(mm)
a
0.4
b
1.5
c
0.5
a
100
Solder Resist (Coat with heat resistant resin for solder)
・Pressurization
Method
20
50min.
Pressurization speed
1.0mm/s
Pressurize
R5
Support
Capacitance meter
45
45
Flexure
Fig.2 (in mm)
Adhesive Strength of Termination, Vibration, Temperature Sudden Change, High Temperature High Humidity(Steady), Durability
・Test
Substrate
Material : JIS C 6484 Copper-clad laminated sheets for PCBs (Glass fabric base, epoxy resin)
Low frequency response of single tube common emitter amplifier circuit If there is no coupling capacitor and bypass capacitor in the single-tube common-emitter amplifier circuit, the amplitude-frequen...
Villagers weave a bamboo bird's nest To celebrate the opening of the Beijing Olympics this year, Shuangxi Rafting Gougou Scenic Area specially invited local skilled craftsmen to weave a "bird's nest" ...
Simulation of Patch Array Antenna with TR module ' s effect
Chengcheng Xie Bhargava Anurag
Agilent TechnologiesEEsofEDA
Abstract: In this paper,a new simulation method of patch arrayantennais introduc...
Received a strange packagedismantle!Then I found a bag of strange black powder with some grayish white in it.
My first reaction was WTF is moldy?!
Then I turned down and saw a long strip of toilet pap...
Sailing is gaining more and more attention. How to use modern technology to assist training and improve competition results is particularly important. Considering the real-time data collection in t...[Details]
Due to the significant increase in electronic devices in automotive and industrial applications, the automotive and industrial markets continue to play an important role in China's electronics in...[Details]
Abstract: In order to generate a stable excitation signal, the design of a digital frequency synthesizer is implemented on FPGA using Verilog hardware language. The design includes accumulator, wav...[Details]
This paper designs a dot matrix LED text display screen that is easy to update, expandable, and low-cost. The way to reduce costs is
① Use the Bluetooth data transmission function of mobile ph...[Details]
Battery life is critical for portable applications. For applications such as smoke detectors, security devices, and thermostats, factory-installed batteries need to last for more than 10 years. The...[Details]
The data collector of the automatic weather station is generally designed based on a single-chip microcomputer or a PC/104 bus controller. It has the characteristics of good compatibility with PC, low...[Details]
PV inverter manufacturer SMA has launched its first DC arc fault circuit interrupter (AFCI) PV inverter and has received UL certification.
The new SunnyBoy AFCI inverter models include 3000-US...[Details]
This controller uses PIC16C54 single-chip microcomputer as the controller, and it is very easy to use: just connect a telephone line to the loudspeaker through the controller, and you can rem...[Details]
Spatial Division Multiplexing (SDM) MIMO processing can significantly improve spectrum efficiency and thus greatly increase the capacity of wireless communication systems. Spatial Division Multip...[Details]
LED light sources have many environmental advantages, but early products still have certain technical bottlenecks in heat dissipation and high brightness design that cannot be broken through....[Details]
The rectified DC voltage is then converted back to AC using power electronics such as insulated gate bipolar transistors.
The output voltage is switched on and off at a high frequency, control...[Details]
0 Introduction
Ultrasonic waves
are mechanical waves with a frequency of more than 20KHz, and the propagation speed in the air is about 340 m/s (at 20°C). Ultrasonic waves can be gene...[Details]
The above is to use MB1404 as a stereo composite signal transmitter. You can use the internal high-frequency amplifier and oscillator or not! According to my experience, I still recommend beginners...[Details]
Cars equipped with xenon headlights are already common on the road. Whether they are standard equipment on high-end cars or embellishments on modified cars, xenon lamps are gradually becoming a sym...[Details]
1 Overview
In the field of traditional lighting, the concepts and definitions of lamps and lamps are clear. Lamps and lamps have their own applicable product standards, supporting technical st...[Details]
Analog electronics
京公网安备 11010802033920号
EEWORLD