1. General
■
■
■
■
■
Monolithic structure provides high reliability in a wide temperature and humidity range
High quality ceramic material and unique manufacturing process provides high Q at high fr
Standard EIA packages: 1E, 1J
Nickel barrier with solder overcoat for excellent solderability
Marking: Brown body color with no marking (1E)
White body color with with black stripe and no marking (1J)
2. Dimensions
W
L
Solder
Plating
Ni
Plating
Silver
Metallization
d
Size
Code
1E
(0402)
1J
(0603)
L
.039±.004
(1.0±0.1)
.063±.006
(1.6±0.15)
Dimensions
inches (mm)
W
t
.02±.004
(0.5±0.1)
.031±.006
(0.8±0.15)
.02±.004
(0.5±0.1)
.031±.006
(0.8±0.15)
t
Terminations
(Metallization
Bands)
d
Electrodes
3. Type Designation
The type designation shall be in the following form:
MHL
Type
1E
Size
1E
1J
C
Material
Permeability
Code:
C
T
T
Termination
Material
T: Sn
(Other termination
styles available,
contact factory
for options)
TE
Packaging
TP: 7" paper tape 2mm pitch
(1E only - 10,000 pcs/reel)
TD: 7" paper tape
(1J - 4,000 pcs/reel
3N9
Nominal
Inductance
3N9 = 3.9nH
R10 = 100nH
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.
Spec ific ation s given herein m ay be c hang ed at an y tim e w itho ut prior not ice. Plea se co nfirm t echn ic al spec ific ations b efore yo u o
MHL1ECTTP1N0*
MHL1ECTTP1N2*
MHL1ECTTP1N5*
MHL1ECTTP1N8*
MHL1ECTTP2N2*
MHL1ECTTP2N7*
MHL1ECTTP3N3*
MHL1ECTTP3N9*
MHL1ECTTP4N7*
MHL1ECTTP5N6*
MHL1ECTTP6N8*
MHL1ECTTP8N2*
MHL1ECTTP10N*
MHL1ECTTP12N*
MHL1ECTTP15N*
MHL1ECTTP18N*
MHL1ECTTP22N*
MHL1ECTTP27N*
MHL1ECTTP33N*
MHL1ECTTP39N*
MHL1ECTTP47N*
MHL1ECTTP56N*
MHL1ECTTP68N*
MHL1ECTTP82N*
MHL1ECTTPR10*
NEW
1.0
1.2
1.5
1.8
2.2
2.7
3.3
3.9
4.7
5.6
6.8
8.2
10
12
15
18
22
27
33
39
47
56
68
82
100
120
1.5
1.8
2.2
2.7
3.3
3.9
4.7
5.6
6.8
8.2
10
12
15
18
22
27
27
33
37
36
10000
0.12
0.13
0.14
0.16
0.17
0.19
0.22
0.24
0.27
0.32
0.37
0.42
0.50
0.55
0.65
0.8
0.9
1.0
1.2
1.3
1.4
S: ±0.3nH
34
6000
4000
32
11
8
31
30
J: ±5%
28
26
24
23
21
19
16
––
––
3900
3500
3200
2600
2300
2000
1600
1400
1200
1100
900
750
300
200
10
180
150
100
600
1.6
MHL1ECTTPR12*
MHL1JCTTD1N5*
MHL1JCTTD1N8*
MHL1JCTTD2N2*
MHL1JCTTD2N7*
MHL1JCTTD3N3*
MHL1JCTTD3N9*
MHL1JCTTD4N7*
MHL1JCTTD5N6*
MHL1JCTTD6N8*
MHL1JCTTD8N2*
MHL1JCTTD10N*
MHL1JCTTD12N*
MHL1JCTTD15N*
MHL1JCTTD18N*
MHL1JCTTD22N*
MHL1JCTTD27N*
MHL1JTTTD27N*
MHL1JCTTD33N*
8
S: ±0.3nH
14
6000
0.10
100
0.13
0.15
0.20
0.23
0.20
0.28
0.30
0.35
0.40
0.45
0.50
0.55
0.60
500
10
46
4000
5800
3200
2600
2300
2000
1600
1400
1200
15
J: ±5%
12
18
15
600
*Add tolerance character (S, J)
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.
Spec ific ation s given herein m ay be c hang ed at an y tim e w itho ut prior not ice. Plea se co nfirm t echn ic al spec ific ations b efore yo u o
MHL1JCTTD39N*
MHL1JTTTD39N*
MHL1JCTTD47N*
MHL1JCTTD56N*
MHL1JCTTD68N*
MHL1JCTTD82N*
MHL1JCTTDR10*
MHL1JCTTDR12*
MHL1JCTTDR15*
MHL1JCTTDR18*
MHL1JCTTDR22*
39
39
47
56
68
82
100
120
150
180
220
15
17
12
J: ±5%
15
46
39
37
36
29
16
1100
900
700
600
500
400
0.65
0.70
0.75
0.80
0.85
0.90
1.0
1.2
1.3
1.5
500
400
300
8
13
—
*Add tolerance character (S, J)
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.
Spe cific at io ns given herein m ay be chan ged at an y tim e w ith out prior not ice. P le ase co nfirm t ech nical spec ific ation s before y ou o
Storage Temperature
40°C @ 70% Humidity
Sealed plastic bags with desiccan
used to reduce the potential of ox
the terminations during storage.
Flux:
5-10 sec dip
After Flux:
Air dry for 15 sec
Preheat:
150°C ±10°C
Preheat Time:
60 sec
Solder Temp:
260°C ±5°C
Dip Time:
10 ±1 sec
Flux:
5-10 sec dip
After Flux:
Air dry for 15 sec
Solder Temp:
245°C ±5°C
Dip Time:
5 ±0.5 sec
Resistance to Solder
Heat
Change in Impedance:
Relative to value before
test ±20%.
Appearance:
There shall be no cracking
Solder Coverage:
More than 75% of the terminal
electrode shall be covered with solder.
Solderability
Solder Coverage:
More than 95% of the
termination shall be covered with solder.
Leach Resistance
Appearance:
There shall be no visible signs of
physical or mechanical damage (i.e. no cracks)
Terminations:
Termination must not be leached
away for more than 5%.
The bead shall be subjected to the
5 steps for the period of time show
The 5 steps constitute one (1) rota
4 rotations shall be carried out.
1) Flux:
5-10 sec
2) After Flux:
Air dry for 15 sec
3) Solder Temp:
230°C ±5°C
4) Dip Time:
5 ±0.5 sec
5) Cool:
Air cool for 60 seconds
Insulation Resistance
Solvent Resistance
Insulation Resistance:
Min 1G ohms
Change in Impedance:
Relative to value before
test ±10%.
Cleaning by:
Washer:
Ultrasonic w
Solvent:
Isopropyl alcohol
Time:
3 minutes
Type
1E
1J
Type
1E
1J
W(kgf)
––
0.5
W(kgf)
––
1.4
Terminal Strength
(hanging test)
Appearance:
The terminal electrode shall not
break off, nor shall there be damage to the body.
30
Terminal Strength
(push test)
Appearance:
There shall be no evidence of
mechanical degradations to terminals or body.
Bending Strength
Appearance:
There shall be no physical or
mechanical damage
Impedance:
Relative to initial value before test ±10%
Board:
90x40x1.6mm
Bend:
1mm
Time:
5 sec
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.
Spec ific ation s given herein m ay be c hang ed at an y tim e w itho ut prior not ice. Plea se co nfirm t echn ic al spec ific ations b efore yo u o
mechanical damage
Impedance:
Relative to initial value before test
±10%
Vibration
Impedance:
Relative to initial value ±10%
Time:
11 msec
There shall be 3 shocks in each o
(18 shocks total).
Only endurance conditioning by s
be made. The entire frequency ra
10-2,000 Hz and return to 10 Hz i
minutes (this shall constitute one
Amplitude: 15G
The test shall have a 15G peak an
applied for a period of 4 hours (12
in each of 3 mutually perpendicula
(a total of 36 cycles within a total o
Step
1-start
2-hold
3-transfer
4-hold
5-transfer
Temperature
-40°C ±2°C
-40°C ±2°C
—
+105°C ±2°C
—
Thermal Shock
Appearance:
There shall be no physical or
mechanical damage.
Impedance:
Relative to initial value ±20%.
DCR:
The DCR shall not exceed initial specified
value.
Testing of the parts will be made at 0 hours, 250
hours and 500 hours. Before testing the parts
shall be allowed to cool to room temperature for
24 hours.
30
0.5
30
0.5
Steps 1 thru 5 constitute one com
and the test shall consist of a tota
cycles.
Temperature:
85°C ±2°C
Relative Humidity:
85%
Time:
1,000 hours total
Apply:
100% rated current
Load Humidity
Appearance:
There shall be no physical or
mechanical damage
Impedance:
Relative to initial value ±15%
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Life Test
Appearance:
There shall be no physical or
mechanical damage
Impedance:
Relative to initial value ±15%
Measurements shall be taken at 0 hours, 250
hours, 500 hours and 1,000 hours and shall meet
the conditions stated above.
Temperature:
85°C ±2°C
Time:
1,000 hours total
Apply:
100% rated current
6. Packaging Specifications
KOA’s multilayer components are provided on tape-and-reel
for use in pick-and-place machines. The reel size is 7 inch.
Bolivar Drive
■
P.O. Box 547
■
Bradford, PA 16701
■
USA
■
814-362-5536
■
Fax 814-362-8883
■
www.
Spec ific ation s given herein m ay be c hang ed at an y tim e w itho ut prior not ice. Plea se co nfirm t echn ic al spec ific ations b efore yo u o
京公网安备 11010802033920号
EEWORLD