SURFACE MOUNT
NPO, X7R, Y5V/Z5U dielectric
All standard chip sizes
13" reel size available
Our range of SMD multi-layer ceramic capacitors compliments the
leaded capacitors available in radial and axial form.
All product packaging is fully marked with date and lot traceability
information.
Most industry standard sizes are available, including 0402 and
1812.
CERAMIC SURFACE MOUNT MULTI - LAYER DS
SECTION 1
OUTLINE DRAWING
T
L
W
L
mm
1.0±0.1
1.6±0.15
2.0±0.2
3.2±0.2
3.2±0.3
4.5±0.3
5.7±0.4
W
mm
0.5±0.05
0.8±0.1
1.25±0.15
1.6±0.15
2.5±0.3
3.2±0.3
5±0.4
T
mm
0.6 MAX
0.9 MAX
1.3 MAX
1.3 MAX
1.7 MAX
1.6 MAX
2.0 MAX
P
mm
0.2
0.3
0.5
0.5
0.5
0.5
0.5
Size Code
0402
0603
0805
1206
1210
1812
2220
Indicates
termination area
Dimensions in mm
P
C
P
TOLERANCES
Dielectric materials, capacitance values and tolerances are only available in the following
combinations.
Dielectric
Available Tolerances
Capacitance
Tolerance Codes
± 0.25pF, ± 0.5pF
E12 Values
B = ± 0.1pF
COG
± 1%
C = ± 0.25pF
± 2%
D = ± 0.5pF
± 5%
F = ± 1%
G = ± 2%
J = ± 5%
K = ± 10%
M = ± 20%
Z = -20 + 80%
X7R/ X5R
± 5%, ± 20%
E12 Values
**
Y5V
± 20%, -20 + 80%
E6 Values
Z5U
± 20%, -20 + 80%
E6 Values
ORDERING INFORMATION
DS
Part
U
Voltage
U = 50/63V
A = 100V
F = 200V
E = 25V
C = 16V
B = 10V
J = 500V
G = 250V
D = 6.3V
005
Size
0402
0603
0805
1206
1210
1812
2220
C
Dielectric
C = NPO
R =- X7R
X = X5R
G = Y5V
W = Z5U
101
Value
Example
101 = 100pF
102 = 1nF
103 = 10nF
104 = 100nF
J
Tolerance
See Above
**
for code
N
Plating
N = Nickel barrier
1
Fax: 01371 875075
www.dubilier.co.uk
Tel: 01371 875758
SURFACE MOUNT
CERAMIC SURFACE MOUNT MULTI - LAYER DS
PERFORMANCE CHARACTERISTICS
PERFROMANCE CHARACTERISTICS
1. ELECTRICAL
Dielectric Code
General
COG
COG dielectrics are very
stable. Temperature, fre-
quency and time vary little.
Typical applications are
in tuned circuits, timing
circuits and fast rise time
circuits.
- 55° to + 125°
> 100G ohms or 1000 sec
whichever is less
50, 100, 200, 500
2.5 x rated voltage
C > 20pf : 0 ± 00ppm/°C
C < 20pF : see CECC 32
101-801
X7R
X5R
Y5V
Z5U
X7R dielectrics offer higher X5R dielectrics offer higher Y5V dielectrics offer the
Z5U dielectrics offer the
capacitance for a given
capacitance for a given
highest capacitance for
highest cpacitance for a
case size than COG.
case size than X7R.
a given case size than X5R. given case size than Y5V.
Applications would include Applictaions would include Applications would include
bypass, coupling and filter- bypass, coupling and filter- bypass and decoupling
ing circuits.
ing circuits.
circuits or where tempera-
ture dependence is not of
major importance.
-55° to + 125°
>100G ohms or 1000 sec
whichever is less
10, 16, 25, 50, 100, 200,
500
2.5 x rated voltage
± 15%
- 55° to + 85°
>100G ohms or 1000sec
whichever is less.
10,16,25,50
2.5 X rated voltage.
± 15%
- 25° to + 85°
>10G ohms or 100 sec
whichever is less.
10, 16, 25, 50, 100
2 x rated voltage
+30% to - 80%
Applications would include
bypass and decoupling
circuits or where tempera-
ture dependance is not of
major importance.
- 25° to + 85°
>10G ohms or 100 sec
whichever is less.
25, 50
2.5 x rated voltage
+22% to - 56%
SECTION 1
Examples of Applications
Temperature Range
Insulation Resistance (I.R.)
after 1 min charging at
Rated Voltage
Voltage Ratings dc
Proof Voltage
Max allowable Capaci-
tance
Variation over Temperature
Range
. ENVIRONMENT
Test
Resistance to soldering
heat
Adhesion
Conditions
Components completely
immersed in a solder bath
at 260 ± 10° for 5 secs.
Component mounted to
substrate a force of 5N
applied normal to the line
joining the termination
and in a line parallel to the
substrate.
- 55 to 125°C, 5 cycles
(1B, 2C1)
- 25 to +85°, 5 cycles
(2F4)
Requirement
25% Max leaching on each
edge
No visible damage
Rapid change or Tem-
perature
No visible damage. After
recovery
∆ C/C
∆ C/C
∆ C/C
∆ C/C
Tan
IR.
≤±1%
or pF
COG
≤±10% X7R
≤±10% X5R
≤±20% Y5V
≤1.5 x speci-
fied value
≤0.25 x speci-
fied value
17
Fax: 01371 875075
www.dubilier.co.uk
Tel: 01371 875758