ELP 58/11/38
Core (without clamp recess)
Core set EELP 58
Combination: ELP 58/11/38 with ELP 58/11/38
■
To IEC 62317-9
■
Delivery mode: single units
B66293
ELP 58/11/38
Magnetic characteristics
(per set)
Σl/A
l
e
A
e
A
min
V
e
= 0.26 mm
–1
= 80.7 mm
= 310 mm
2
= 308 mm
2
= 25000 mm
3
Approx. weight
130 g/set
Ungapped
Material A
L
value
nH
N87
7400
±25%
μ
e
1540
B
S
*
mT
300
P
V
W/set
Ordering code
(per piece)
< 15.0 (200 mT, 100 kHz, 100 °C) B66293G0000X187
* H = 250 A/m; f = 10 kHz; T = 100 °C
Other A
L
values/air gaps and materials available on request – see Processing remarks on page 4.
Calculation factors
(for formulas, see
“E cores: general information”
)
EELP 58:
Material
Relationship between
air gap – A
L
value
K1 (25 °C)
N87
Validity range:
521
K2 (25 °C)
–0.732
Calculation of saturation current
K3 (25 °C)
763
K4 (25 °C)
–0.796
K3 (100 °C) K4 (100 °C)
705
–0.873
K1, K2: 0.10 mm < s < 1.50 mm
K3, K4: 50 nH < A
L
< 500 nH
Please read
Cautions and warnings
and
Important notes
at the end of this document.
2
5/17
ELP 58/11/38 with I 58/4/38
Core (without clamp recess)
Core set EILP 58
Combination:
ELP 58/11/38 with I 58/4/38
■
To IEC 62317-9
■
Delivery mode: single units
B66293
ELP 58/11/38
I 58/4/38
Magnetic characteristics
(per set)
Σl/A
l
e
A
e
A
min
V
e
= 0.22 mm
–1
= 67.7 mm
= 310 mm
2
= 308 mm
2
= 21000 mm
3
Approx. weight
110 g/set
Ungapped
Mate- A
L
value
μ
e
nH
rial
N87
8400
±25%
B
S
*
mT
P
V
W/set
Ordering code
(per piece)
1450 300
< 13.0 (200 mT, 100 kHz, 100 °C) B66293G0000X187 (ELP core)
B66293K0000X187 (I core)**
* H = 250 A/m; f = 10 kHz; T = 100 °C
** Plate-type tool
Other A
L
values/air gaps and materials available on request - see Processing remarks on page 4.
Calculation factors
(for formulas, see
“E cores: general information”
)
EILP 58:
Material
Relationship between
air gap – A
L
value
K1 (25 °C)
N87
Validity range:
591
K2 (25 °C)
–0.685
Calculation of saturation current
K3 (25 °C)
791
K4 (25 °C)
–0.796
K3 (100 °C) K4 (100 °C)
721
–0.873
K1, K2: 0.10 mm < s < 1.50 mm
K3, K4: 50 nH < A
L
< 500 nH
Please read
Cautions and warnings
and
Important notes
at the end of this document.
3
5/17
Ferrites and accessories
Cautions and warnings
Cautions and warnings
Mechanical stress and mounting
Ferrite cores have to meet mechanical requirements during assembling and for a growing number
of applications. Since ferrites are ceramic materials one has to be aware of the special behavior
under mechanical load.
As valid for any ceramic material, ferrite cores are brittle and sensitive to any shock, fast tempera-
ture changing or tensile load. Especially high cooling rates under ultrasonic cleaning and high static
or cyclic loads can cause cracks or failure of the ferrite cores.
For detailed information see data book, chapter
“General - Definitions, 8.1”.
Effects of core combination on A
L
value
Stresses in the core affect not only the mechanical but also the magnetic properties. It is apparent
that the initial permeability is dependent on the stress state of the core. The higher the stresses are
in the core, the lower is the value for the initial permeability. Thus the embedding medium should
have the greatest possible elasticity.
For detailed information see data book, chapter
“General - Definitions, 8.1”.
Heating up
Ferrites can run hot during operation at higher flux densities and higher frequencies.
NiZn-materials
The magnetic properties of NiZn-materials can change irreversible in high magnetic fields.
Ferrite Accessories
EPCOS ferrite accessories have been designed and evaluated only in combination with EPCOS
ferrite cores. EPCOS explicitly points out that EPCOS ferrite accessories or EPCOS ferrite cores
may not be compatible with those of other manufacturers. Any such combination requires prior te-
sting by the customer and will be at the customer‘s own risk.
EPCOS assumes no warranty or reliability for the combination of EPCOS ferrite accessories with
cores and other accessories from any other manufacturer.
Processing remarks
The start of the winding process should be soft. Else the flanges may be destroyed.
– Too strong winding forces may blast the flanges or squeeze the tube that the cores can not be
mounted any more.
– Too long soldering time at high temperature (>300 °C) may effect coplanarity or pin arrange-
ment.
– Not following the processing notes for soldering of the J-leg terminals may cause solderability
problems at the transformer because of pollution with Sn oxyde of the tin bath or burned insula-
tion of the wire. For detailed information see chapter
“Processing notes”,
section 2.2.
– The dimensions of the hole arrangement have fixed values and should be understood as
a recommendation for drilling the printed circuit board. For dimensioning the pins, the group
of holes can only be seen under certain conditions, as they fit into the given hole arrangement.
To avoid problems when mounting the transformer, the manufacturing tolerances for positioning
the customers’ drilling process must be considered by increasing the hole diameter.
Please read
Cautions and warnings
and
Important notes
at the end of this document.
4
5/17
Ferrites and accessories
Cautions and warnings
Display of ordering codes for EPCOS products
The ordering code for one and the same product can be represented differently in data sheets,
data books, other publications and the website of EPCOS, or in order-related documents such as
shipping notes, order confirmations and product labels.
The varying representations of the
ordering codes are due to different processes employed and do not affect the
specifications of the respective products.
Detailed information can be found on the Internet
under www.epcos.com/orderingcodes.
Please read
Cautions and warnings
and
Important notes
at the end of this document.
5
5/17
Power technology
京公网安备 11010802033920号
EEWORLD